A high flowability TPU95A-HF flexible 3D printing material
Product Description
FusFlex™️ TPU95A-HF is TPU material that is easy to print. FusFlex™️ TPU95A-HF is easier to be extruded than other conventional TPU consumables under the same hardness. When a suitable extruder is selected, FusFlex™️ TPU95A-HF can support a printing speed of more than 100mm/s.
Material Properties
Recommended printing conditions
Nozzle Temperature | 210-230 °C |
Recommended Nozzle Diameter | ≥0.2mm |
Recommended build surface treatment | PEI or Coating with PVP glue |
Build plate temperature | 20-50 °C |
Chamber Temp | N/A |
Cooling fan speed | On |
Print speed | 30-120 mm/s |
Retraction distance | 1-5 mm |
Retraction speed | 1800-3600 mm/min |
Recommended Support Material | FusFree™ S-Multi Quick-Remove Support |
Drying setting | 70-80℃ for 4-6h |
Annealing | N/A |
Printing Tips：
If you want to achieve high-speed printing, it is recommended to use direct extruders, such as BMG extruder, Titan extruder and Hemera extruder, and appropriately increase the nozzle temperature.
TPU material is very easy to absorb moisture when exposed to air, and printing after absorbing moisture will result ozzing, extruding with bubbles and rough surface appearance, thus reducing print quality. It is recommended that put the filament into a dry box (humidity below 15%) immediately after opening the FusFlex™ TPU95A-HF vacuum foil bag for printing. Please put the unused filament back into the original aluminum foil bag for sealed storage.
After the material is damp, there will be more printing ozzing, bubbles extruded and rough printing surface. Please dry the filament in an oven at 70-80℃ for 4-6h to restore the printing quality of FusFlex™ TPU95A-HF.