FusRock Material Table

Product	Application scenarios	Tensile strength(X-Y)	Young’s modulus(X-Y)	Elongation at break (X-Y)	Bending strength (X-Y)	Bending modulus (X-Y)	Charpy impact strength （X-Y）	Tensile strength (Z)	Young’s modulus (Z)	Elongation at break (Z)	Determination of temperature (0.45 MPa)	Determination of temperature (1.8 MPa)	Recommended to maximize the extrusion flow	Nozzle material requirements	Whether to support AMS	Whether to seal the box	Sealed drying box with RH Below 15%	Annealing treatment
ToughPETG-HF	General application	44.23±0.64 MPa	1821.82±49.41 MPa	14.04±7.77 %	71.40±0.74 MPa	1895.07±36.19 MPa	16.39±2.16 KJ/m²	42.70±0.51 MPa	1955.67±179.30 MPa	4.51±0.82 %	70 ℃	65 ℃	28mm³/s	Brass nozzle, copper alloy nozzle	Yes	No	Recommend	No need for annealing
PETG-CF	General application	46.11±0.75 MPa	2616±25 MPa	5.53±0.22 %	66.80±1.32 MPa	2291±42 MPa	5.11±1.01 KJ/m²	25.1±1.9 MPa	1856±41 MPa	1.81±0.3 %	77 ℃	74 ℃	24mm³/s	Stainless steel nozzle, hardened steel nozzle, tungsten carbide nozzle	Yes	No	Recommend	No need for annealing
PETG-CF HF	General application	53.15±0.38 MPa	3062.70±42.96 MPa	5.88±0.69 %	85.11±0.54 MPa	3013.81±57.08 MPa	3.52±0.47 KJ/m²	30.29±1.19 MPa	2170.34±46.05 MPa	1.62±1.0 %	71 ℃	68 ℃	28mm³/s	Stainless steel nozzle, hardened steel nozzle, tungsten carbide nozzle	Yes	No	Recommend	No need for annealing
PETG-Matte	General application	48.79±0.3 MPa	2247±37 MPa	8.43±2.53 %	68.27±0.89 MPa	2144.44±35.54 MPa	5.64±1.29 KJ/m²	28.56±2.04 MPa	1813±72 MPa	2.01±0.22 %	73 ℃	68 ℃	24mm³/s	Stainless steel nozzle, hardened steel nozzle, tungsten carbide nozzle	Yes	No	Recommend	No need for annealing
ASA	Outdoor application	38.5±1.6 MPa	2317±246 MPa	5.2±1.4 %	64.49±1.3 MPa	2399±147 MPa	12.9±0.9 KJ/m²	27.87±0.4 MPa	2037±64 MPa	2.43±0.27 %	93 ℃	83 ℃	24mm³/s	Brass nozzle, copper alloy nozzle	Yes	Yes	Recommend	No need for annealing
ABS	Low odor\General application	38.96±0.33 MPa	2384.22±20.0 MPa	5.77±0.84 %	67.81±0.54 MPa	2400±79.69 MPa	20.03±1.32 KJ/m²	32.25±0.72 MPa	2201.74±74.91 MPa	2.70±0.59 %	92 ℃	86 ℃	24mm³/s	Brass nozzle, copper alloy nozzle	Yes	Yes	Recommend	No need for annealing
ABS-HF	General application	37.13±0.59 MPa	2115.10±24.02 MPa	3.65±1.52 %	57.46±0.25 MPa	2117.02±32.46 MPa	23.16±2.32 KJ/m²	33.48±0.23 MPa	2097.03±37.77 MPa	4.07±0.57 %	72 ℃	65 ℃	28mm³/s	Brass nozzle, copper alloy nozzle	Yes	No	Recommend	No need for annealing
ABS-GF	General application	43.44±0.86 MPa	3213±82.78 MPa	2.80±0.21 %	66.21±0.42 MPa	2681±24.99 MPa	8.17±0.66 KJ/m²	19.02±0.9 MPa	2331±130 MPa	1.28±0.32 %	96 ℃	92 ℃	24mm³/s	Stainless steel nozzle, hardened steel nozzle, tungsten carbide nozzle	Yes	Yes	Recommend	No need for annealing
PLA-Aero Pro	Outdoor aerial vehicle	16.87±2.11 Mpa MPa	820.31±8.82 MPa	9.17±0.61 %	19.27±0.09 MPa	872.93±55.10 MPa	2.93±0.15 KJ/m²	-	254±23 MPa	10.91±1.11 %	50 ℃	43 ℃	6mm³/s	Brass nozzle, copper alloy nozzle	Yes	No	Recommend	No need for annealing
ASA-Aero	Outdoor aerial vehicle\Thermal insulation cover	8.25±0.15 MPa	593.99±24.34 MPa	11.52±0.58 %	14.31±1.66 MPa	544.92±74.44 MPa	2.29±0.13 KJ/m²	7.86±0.14 MPa	457.94±20.84 MPa	5.54±0.28 %	70 ℃	55 ℃	6mm³/s	Brass nozzle, copper alloy nozzle	Yes	Yes	Recommend	No need for annealing
TPU78D	High toughness	43.79±0.99 MPa	419.41±7.31 MPa	270.15±8.32 %	16.52±0.55 MPa	450.05±59.93 MPa	Not broken	17.69±0.49 MPa	418.53±35.72 MPa	33.84±9.01 %	-	-	12mm³/s	Brass nozzle, copper alloy nozzle	Yes	No	Recommend	No need for annealing
TPU95A-HF	Flexible application	31.81±3.26 MPa	-	471±81 %	-	-	-	-	-	-	-	-	9mm³/s	Brass nozzle, copper alloy nozzle	No	No	Recommend	No need for annealing
TPU85A-HF	Flexible application	23.44±2.70 MPa	-	564±35 %	-	-	-	-	-	-	-	-	6mm³/s	Brass nozzle, copper alloy nozzle	No	No	Recommend	No need for annealing
TPU75A	Flexible application	19.25±0.66 Mpa MPa	-	527±10.61 %	-	-	-	-	-	-	-	-	-	Brass nozzle, copper alloy nozzle	No	No	Recommend	No need for annealing
TPU65A	Flexible application	10.63±0.31 Mpa MPa	-	600±39 %	-	-	-	-	-	-	-	-	-	Brass nozzle, copper alloy nozzle	No	No	Recommend	No need for annealing
PC/ABS-FR	Flame-retardant thin-walled parts	52.51±0.2 MPa	2588.73±64.81 MPa	5.55±0.9 %	85.95±0.83 MPa	2504.55±22.88 MPa	8.39±0.46 KJ/m²	34.26±0.84 MPa	2302.81±46.92 MPa	1.88±0.11 %	88 ℃	83 ℃	32mm³/s	Brass nozzle, copper alloy nozzle	Yes	Yes	Recommend	No need for annealing
PET-GF	General structural appearance parts	70.86±2.86 MPa	4130.13±107.0 MPa	2.56±0.30 %	114.87±3.0 MPa	3650.32±65.81 MPa	6.56±0.68 KJ/m²	33.95±2.38 MPa	3322.37±94.04 MPa	1.14±0.11 %	120.3 ℃	99.1 ℃	20mm³/s	Stainless steel nozzle, hardened steel nozzle, tungsten carbide nozzle	Yes	No	Must	Can be annealing
PET-CF	Forced structural parts	70.82±2.74 MPa	6208.45±462.92 MPa	1.46±0.10 %	110.79±3.36 MPa	5588.24±363.94 MPa	4.59±0.15 KJ/m²	34.13±0.93 MPa	3270.44±62.77 MPa	1.20±0.04 %	175.4 ℃	115.6 ℃	20mm³/s	Hardened steel nozzle, tungsten carbide nozzle	No	No	Must	Can be annealing
PET-CF Lite	Forced structural parts	62.42±0.63 MPa	4663.08±294.9 MPa	2.83±0.29 %	94.44±4.27 MPa	4450.32±78.36 MPa	6.43±0.28 KJ/m²	30.46±1.55 MPa	3338.76±186.95 MPa	1.0±0.10 %	90.2 ℃	78.4 ℃	16mm³/s	Stainless steel nozzle, hardened steel nozzle, tungsten carbide nozzle	Yes	No	Must	No need for annealing
PAHT	High-gloss self-lubrication requires structural parts and gear parts	69.29±1.17 MPa	3329.72±235.60 MPa	9.77±1.68 %	112.64±1.60 MPa	3202.24±115.78 MPa	9.74±0.84 KJ/m²	50.03±2.30 MPa	-	-	79.6 ℃	72.5 ℃	12mm³/s	Stainless steel nozzle, hardened steel nozzle, tungsten carbide nozzle	Yes	No	Must	No need for annealing
PAHT-GF	Temperature-resistant insulation structural parts and wear-resistant parts	90.50±2.57 MPa	5375.42±244.39 MPa	2.28±0.10 %	140.77±5.28 MPa	4897.64±136.40 MPa	5.84±0.37 KJ/m²	59.58±1.71 MPa	3952.22±135.01 MPa	1.78±0.07 %	180.2 ℃	109.4 ℃	20mm³/s	Hardened steel nozzle, tungsten carbide nozzle	No	No	Must	Can be annealing
PAHT-CF	High-temperature and high-strength structural appearance parts, wear-resistant parts	95.53±3.62 MPa	8114.10±539.02 MPa	1.52±0.11 %	141.82±4.34 MPa	7098.40±440.49 MPa	5.62±0.67 KJ/m²	51.03±2.18 MPa	3869.82±174.36 MPa	1.56±0.07 %	190.7 ℃	117.5 ℃	20mm³/s	Hardened steel nozzle, tungsten carbide nozzle	No	No	Must	Can be annealing
NexABS-GF25	Structural appearance parts with temperature resistance below 90℃, low odor	48.48±0.61 MPa	3752.13±68.39 MPa	2.10±0.10 %	78.80±1.26 MPa	3531.71±75.79 MPa	8.91±0.63 KJ/m²	30.48±0.47 MPa	2843.56±69.90 MPa	2.20±0.44 %	87 ℃	81 ℃	24mm³/s	Stainless steel nozzle, hardened steel nozzle, tungsten carbide nozzle	Yes	Yes	Recommend	No need for annealing
NexABS-CF20	Structural appearance parts with temperature resistance below 90℃, high rigidity requirements	47.86±2.32 MPa	4606.28±192.38 MPa	1.48±0.11 %	80.21±0.55 MPa	4365.286±153.79 MPa	8.12±0.78 KJ/m²	28.21±0.35 MPa	2713.50±88.38 MPa	1.81±0.16 %	90 ℃	83 ℃	24mm³/s	Stainless steel nozzle, hardened steel nozzle, tungsten carbide nozzle	Yes	Yes	Recommend	No need for annealing
NexASA-CF20	Temperature resistance below 100℃ structural appearance parts, high rigidity requirements	50.06±1.0 MPa	4502.58±103.44 MPa	1.64±0.11 %	84.30±1.37 MPa	4537.67±264.85 MPa	5.76±0.17 KJ/m²	31.03±2.18 MPa	2570.8±130.85 MPa	1.50±0.14 %	101.1 ℃	95.8 ℃	20mm³/s	Stainless steel nozzle, hardened steel nozzle, tungsten carbide nozzle	Yes	Yes	Recommend	No need for annealing
NexPA-GF25	High-temperature and high-strength structural parts and wear-resistant parts	105.01±1.14 MPa	5729.78±301.68 MPa	2.41±0.05 %	168.20±4.76 MPa	5957.97±95.66 MPa	7.59±0.81 KJ/m²	65.4±2.99 MPa	4150.79±80.04 MPa	1.90±0.15 %	195.5 ℃	118 ℃	24mm³/s	Hardened steel nozzle, tungsten carbide nozzle	No	No	Must	Can be annealing
NexPA-CF25	High-temperature and high-strength structural parts, high-rigidity requirements, wear-resistant parts	118.19±3.82 MPa	9989.47±227.73 MPa	1.62±0.12 %	184.19±5.73 MPa	9214.34±249.80 MPa	7.29±0.76 KJ/m²	58.01±2.05 MPa	4213.72±97.08 MPa	1.64±0.10 %	196.9 ℃	124.2 ℃	24mm³/s	Hardened steel nozzle, tungsten carbide nozzle	No	No	Must	Can be annealing
NexPPS-CF	High-temperature and strong corrosive environmental parts	47.26±0.08 MPa	4700.94±109.36 MPa	1.65±0.08 %	80.89±2.10 MPa	4713.11±186.92 MPa	5.99±0.39 KJ/m²	27.75±3.26 MPa	3250.38±294.96 MPa	1.06±0.22 %	190.1 ℃	137.8 ℃	24mm³/s	Hardened steel nozzle, tungsten carbide nozzle	No	No	Must	Can be annealing
Product	Application scenarios	Tensile strength(X-Y)	Young’s modulus(X-Y)	Elongation at break (X-Y)	Bending strength (X-Y)	Bending modulus (X-Y)	Charpy impact strength （X-Y）	Tensile strength (Z)	Young’s modulus (Z)	Elongation at break (Z)	Determination of temperature (0.45 MPa)	Determination of temperature (1.8 MPa)	Recommended to maximize the extrusion flow	Nozzle material requirements	Whether to support AMS	Whether to seal the box	Sealed drying box with RH Below 15%	Annealing treatment

2024-03-10

FusRock Material Table

FUSE REAL

ROCK FUTURE

Explore

Latest News

FusRock TCT 2024 China

FusRock TCT 2023 China

Newsletter